聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne 41 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 41 is designed to meet the critical low-temperature impact requirements called out in many automotive specifications.

 

Typical Applications/End Uses:

Vydyne 41 may be used in both industrial and automotive applications. Typical end uses include: clips, fasteners, engine gearing, cable ties, electrical connectors and many other parts that require high-impact properties. Vydyne 41 resins can in many cases be used as metal replacements, offering improvements on abrasion resistance, reduction in part weight, greater processing flexibility and lower energy consumption.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

UL 黄卡 2 •  E70062-100757207

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

添加剂 • 冲击改性剂

• 冲击改性 • 可加工性，良好 • 耐化学性良好

特性 • 抗溶剂性 • 良好耐磨损性 • 耐汽油性

• 抗撞击性，高 • 耐低温冲击 • 耐油性能

• 齿轮 • 紧固件 • 消费品应用领域

用途 • 电气/电子应用领域 • 连接器

• 工业应用 • 汽车领域的应用

机构评级 • ASTM D 4066 PA0171 • ASTM D 6779 PA0171

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.08 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 23°C, 2.00 mm 1.6 -- %

流动方向 : 23°C, 2.00 mm 1.8 -- %

吸水率 ISO 62

23°C, 24 hr 1.0 -- %

平衡, 23°C, 50% RH 2.1 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 1860 1390 MPa ISO 527-2

拉伸应力 ISO 527-2

屈服, 23°C 50.0 35.0 MPa

断裂, 23°C 43.0 39.0 MPa

拉伸应变 (断裂, 23°C) 50 180 % ISO 527-2

弯曲模量 (23°C) 1750 545 MPa ISO 178

弯曲应力 (23°C) 53.0 17.0 MPa ISO 178

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179

-40°C 20 25 kJ/m²

-30°C 35 25 kJ/m²

23°C 76 110 kJ/m²

 

Vydyne® 41

聚酰胺66

Ascend Performance Materials Operations LLC

冲击性能 干燥 调节后的 单位制 测试方法

简支梁无缺口冲击强度 ISO 179

-30°C 无断裂 无断裂

23°C 无断裂 无断裂

悬壁梁缺口冲击强度 ISO 180

-40°C 22 25 kJ/m²

-30°C 40 29 kJ/m²

23°C 78 88 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 145 -- °C ISO 75-2/B

1.8 MPa, 未退火 58.0 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C, 2.00 mm 1.7E-4 -- cm/cm/°C

横向 : 23 到 55°C, 2.00 mm 1.5E-4 -- cm/cm/°C

RTI Elec UL 746

0.750 mm 125 -- °C

1.50 mm 125 -- °C

3.00 mm 125 -- °C

RTI Imp UL 746

0.750 mm 75.0 -- °C

1.50 mm 75.0 -- °C

3.00 mm 75.0 -- °C

RTI UL 746

0.750 mm 85.0 -- °C

1.50 mm 85.0 -- °C

3.00 mm 85.0 -- °C

电气性能 干燥 调节后的 单位制 测试方法

体积电阻率 (0.750 mm) 1.0E+11 -- ohm•cm IEC 60093

介电强度 (1.00 mm) 26 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 5 -- ASTM D495

漏电起痕指数 (3.00 mm) 600 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.750 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 0 -- UL 746

热丝引燃 (HWI) UL 746

0.750 mm PLC 4 --

1.50 mm PLC 3 --

3.00 mm PLC 3 --

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.750 mm HB --

1.50 mm HB --

3.00 mm HB --

灼热丝易燃指数 IEC 60695-2-12

0.750 mm 750 -- °C

1.50 mm 700 -- °C

3.00 mm 700 -- °C

 

Vydyne® 41

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制   测试方法

热灯丝点火温度 IEC 60695-2-13

0.750 mm 775 -- °C

1.50 mm 725 -- °C

3.00 mm 725 -- °C

注射 干燥单位制

干燥温度 80.0°C

干燥时间 4.0hr

建议的最大回制料比例 25%

料筒后部温度 280 到 310°C

料筒中部温度 280 到 310°C

料筒前部温度 280 到 310°C

射嘴温度 280 到 310°C

加工（熔体）温度 285 到 305°C

模具温度 65.0 到 95.0°C

 

 

 

 

 

 